Yunxia GUO
,
Jie LIU
,
Jieying LIANG
,
null
材料科学技术（英）
Surface of polyacrylonitrile (PAN)-based carbon fibers was modified by electrochemical oxidation. The modification effect on carbon fibers surface was explored using atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD). Results showed that on the modified surface of carbon fibers, the carbon contents decreased by 9.7% and the oxygen and nitrogen contents increased by 53.8% and 7.5 times, respectively. The surface roughness and the hydroxyl and carbonyl contents also increased. The surface orientation index was reduced by 1.5% which decreased tensile strength of carbon fibers by 8.1%, and the microcrystalline dimension also decreased which increased the active sites of carbon fiber surface by 78%. The physical and chemical properties of carbon fibers surface were modified through the electrochemical oxidative method, which improved the cohesiveness between the fibers and resin matrix and increased the interlaminar shear strength (ILSS) of carbon fibers reinforced epoxy composite (CFRP) over 20%.
关键词:
Polyacrylonitrile (PAN)
,
null
,
null
,
null
顾书英
,
吴琪琳
,
任杰
新型炭材料
通过稳定化、炭化静电纺制的聚丙烯腈(PAN)前驱体纤维制备了直径为100nm～300nm的纳米炭纤维.用扫描电镜(SEM)、场发射扫描电镜(FESEM)、扫描隧道显微镜(STM)及扫描量热分析法(DSC)研究了纳米炭纤维及其前驱体纤维的形貌及结构.结果表明:纳米炭纤维及其前驱体纤维的直径表现为对数正态分布.静电纺制纤维的环化放热峰移向低温,表明静电纺制纤维可在较低的温度下引发环化.由于静电纺制纤维的粗糙表面及在热处理过程中的收缩行为,在纳米炭纤维表面形成了长度为10nm宽度为5nm的凹坑.
关键词:
纳米炭纤维
,
聚丙烯腈(PAN)
,
静电纺丝,形貌